119不銹鋼的化學(xué)成分表（2）
發(fā)布時間：2012.06.13 新聞來源：不銹鋼酸冼鈍化液|不銹鋼酸洗鈍化膏|不銹鋼酸洗劑|不銹鋼表面處理-天長市俊武不銹鋼表面處理材料廠 瀏覽次數(shù)：
|
類型 |
序號 |
牌 號 |
化學(xué)成分 % | ||||||||||
|
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
Cu |
N |
其它 | |||
|
奧
氏
體
型 |
1 |
1Cr17Mn6Ni5N |
≤0.15 |
≤1.00 |
5.50－7.50 |
≤0.060 |
≤0.030 |
3.50-5.50 |
16.00-18.00 |
- |
- |
≤0.25 |
- |
|
2 |
1Cr18Mn8Ni5N |
≤0.15 |
≤1.00 |
7.50-10.00 |
≤0.060 |
≤0.030 |
4.00-6.00 |
17.00-19.00 |
- |
- |
≤0.25 |
－ | |
|
3 |
1Cr18Mn10Ni5Mo3N |
≤0.15 |
≤1.00 |
8.50-12.00 |
≤0.060 |
≤0.030 |
4.00-6.00 |
17.00-19.00 |
2.8-3.5 |
- |
0.20-0.30 |
- | |
|
4 |
1Cr17Ni7 |
≤0.15 |
≤1.00 |
≤2.00 |
≤0.065 |
≤0.030 |
6.00-8.00 |
16.00-18.00 |
- |
- |
- |
- | |
|
5 |
1Cr18Ni9 |
≤0.15 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
8.00-10.00 |
17.00-19.00 |
- |
- |
- |
- | |
|
6 |
Y1Cr18Ni9 |
≤0.15 |
≤1.00 |
≤2.00 |
≤0.20 |
≤0.030 |
8.00-10.00 |
17.00-19.00 |
1) |
- |
- |
- | |
|
7 |
Y1Cr18Ni9Se |
≤0.15 |
≤1.00 |
≤2.00 |
≤0.20 |
≤0.030 |
8.00-10.00 |
17.00-19.00 |
- |
- |
- |
Se≥0.15 | |
|
8 |
0Cr18Ni9 |
≤0.07 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
8.00-10.00 |
17.00-19.00 |
- |
- |
- |
- | |
|
9 |
00Cr19Ni10 |
≤0.030 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
8.00-10.00 |
18.00-20.00 |
- |
- |
- |
- | |
|
10 |
0Cr19Ni9N |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
7.00-10.50 |
18.00-20.00 |
- |
- |
0.10-0.25 |
- | |
|
11 |
0Cr18Ni10NbN |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
7.50-10.50 |
18.00-20.00 |
- |
- |
0.15-0.30 |
Nb≤0.15 | |
|
12 |
00Cr18Ni10N |
≤0.030 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
8.50-11.50 |
17.00-19.00 |
- |
- |
0.12-0.22 |
- | |
|
13 |
1Cr18Ni12 |
≤0.12 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
10.50-13.00 |
17.00-19.00 |
- |
- |
- |
- | |
|
14 |
0Cr23Ni13 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
12.00-15.00 |
22.00-24.00 |
- |
- |
- |
- | |
|
15 |
0Cr25Ni20 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
19.00-22.00 |
24.00-26.00 |
- |
- |
- |
- | |
|
16 |
0Cr17Ni12Mo2 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
10.00-14.00 |
16.00-18.50 |
2.00-3.00 |
- |
- |
- | |
|
17 |
1Cr18Ni12Mo2Ti6) |
≤0.12 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00-14.00 |
16.00-19.00 |
1.80-2.50 |
- |
- |
Ti5(C%-0.02)~0.08 | |
|
18 |
0Cr18Ni12Mo2Ti |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00-14.00 |
16.00-19.00 |
1.80-2.50 |
- |
- |
Ti5*C%-0.70 | |
|
19 |
00Cr17Ni14Mo2 |
≤0.030 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
12.00-15.00 |
16.00-18.00 |
2.00-3.00 |
- |
- |
- | |
|
20 |
0Cr17Ni12Mo2N |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
10.00-14.00 |
16.00-18.00 |
2.00-3.00 |
- |
0.10-0.22 |
- | |
|
21 |
00Cr17Ni13Mo2N |
≤0.030 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
10.50-14.50 |
16.00-18.50 |
2.00-3.00 |
- |
0.12-0.22 |
- | |
|
22 |
0Cr18Ni12Mo2Cu2 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
10.00-14.50 |
17.00-19.00 |
1.20-2.75 |
1.00-2.50 |
- |
- | |
|
23 |
00Cr18Ni14Mo2Cu2 |
≤0.030 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
12.00-16.00 |
17.00-19.00 |
1.20-2.75 |
1.00-2.50 |
- |
- | |
|
24 |
0Cr19Ni13Mo3 |
≤0.12 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00-15.00 |
18.00-20.00 |
3.00-4.00 |
- |
- |
- | |
|
25 |
00Cr19Ni13Mo3 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00-15.00 |
18.00-20.00 |
3.00-4.00 |
- |
- |
- | |
|
26 |
1Cr18Ni12Mo3Ti6) |
≤0.12 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00-14.00 |
16.00-19.00 |
2.50-3.50 |
- |
- |
Ti5(C%-0.02)~0.08 | |
|
27 |
0Cr18Ni12Mo3Ti |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00-14.00 |
16.00-19.00 |
2.50-3.50 |
- |
- |
Ti5*C%-0.70 | |
|
28 |
0Cr18Ni16Mo5 |
≤0.040 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
15.00-17.00 |
16.00-19.00 |
4.00-6.00 |
- |
- |
- | |
|
29 |
1Cr18Ni9Ti6) |
≤0.12 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
8.00-11.00 |
17.00-19.00 |
- |
- |
- |
Ti5(C%-0.02)~0.08 | |
|
30 |
0Cr18Ni10Ti |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
9.00-12.00 |
17.00-19.00 |
- |
- |
- |
Ti≥5*C% | |
|
31 |
0Cr18Ni11Nb |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
9.00-13.00 |
17.00-19.00 |
- |
- |
- |
Nb≥10*C% | |
|
32 |
0Cr18Ni9Cu3 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
8.50-10.50 |
17.00-19.00 |
- |
3.00-4.00 |
- |
- | |
|
33 |
0Cr18Ni13Si4 |
≤0.08 |
3.00-5.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.50-15.00 |
15.00-20.00 |
- |
- |
- |
2) | |
|
奧氏 體
|
鐵素體型 |
34 |
0Cr26Ni5Mo2 |
≤0.08 |
≤1.00 |
≤1.50 |
≤0.035 |
≤0.030 |
3.00-6.00 |
23.00-28.00 |
1.00-3.00 |
- |
- |
2) |
|
35 |
1Cr18Ni11Si4AlTi |
0.10-0.18 |
3.40-4.00 |
≤0.80 |
≤0.035 |
≤0.030 |
10.--120.. |
17.50-19.50 |
- |
- |
- |
Al 0.10-0.30; Ti 0.40-0.70 | |
|
36 |
00Cr18Ni5MoSi2 |
≤0.030 |
1.30-2.00 |
1.00-2.00 |
≤0.035 |
≤0.030 |
4.50-5.50 |
18.00-19.50 |
2.50-3.00 |
- |
- |
- | |
|
鐵
素
體
型 |
37 |
0Cr13Al |
≤0.08 |
≤1.00 |
≤1.00 |
≤0.035 |
≤0.030 |
3) |
11.50-14.50 |
- |
- |
- |
Al 0.10-0.30 |
|
38 |
00Cr12 |
≤0.030 |
≤1.00 |
≤1.00 |
≤0.035 |
≤0.030 |
3) |
11.00-13.00 |
- |
- |
- |
- | |
|
39 |
1Cr17 |
≤0.12 |
≤0.75 |
≤1.25 |
≤0.035 |
≤0.030 |
3) |
16.00-18.00 |
- |
- |
- |
- | |
|
40 |
Y1Cr17 |
≤0.12 |
≤1.00 |
≤1.00 |
≤0.035 |
≥0.15 |
3) |
16.00-18.00 |
1) |
- |
- |
- | |
|
41 |
1Cr17Mo |
≤0.12 |
≤1.00 |
≤1.00 |
≤0.035 |
≤0.030 |
3) |
16.00-18.00 |
0.75-1.25 |
- |
- |
- | |
|
42 |
00Cr30Mo25) |
≤0.010 |
≤0.40 |
≤0.40 |
≤0.035 |
≤0.030 |
- |
28.50-32.00 |
1.50-2.50 |
- |
≤0.015 |
- | |
|
43 |
00Cr27Mo25 |
≤0.010 |
≤0.40 |
≤0.40 |
≤0.035 |
≤0.030 |
- |
25.00-27.50 |
0.75-1.50 |
- |
≤0.015 |
- | |
|
馬
氏
體
型 |
44 |
1Cr12 |
≤0.15 |
≤0.50 |
≤1.00 |
≤0.035 |
≤0.030 |
3) |
11.50-13.00 |
- |
- |
- |
- |
|
45 |
1Cr13 |
≤0.15 |
≤1.00 |
≤1.00 |
≤0.035 |
≤0.030 |
3) |
11.50-13.50 |
- |
- |
- |
- | |
|
46 |
0Cr13 |
≤0.08 |
≤1.00 |
≤1.00 |
≤0.035 |
≤0.030 |
3) |
11.50-13.50 |
- |
- |
- |
- | |
|
47 |
Y1Cr13 |
≤0.15 |
≤1.00 |
≤1.25 |
≤0.035 |
≥0.15 |
3) |
12.00-14.00 |
1) |
- |
- |
- | |
|
48 |
1Cr13Mo |
≤0.08-0.18 |
≤0.60 |
≤1.00 |
≤0.035 |
≤0.030 |
3) |
11.50-14.00 |
0.30-0.60 |
- |
- |
- | |
|
49 |
2Cr13 |
0.16-0.25 |
≤1.00 |
≤1.00 |
≤0.035 |
≤0.030 |
3) |
12.00-14.00 |
- |
- |
- |
- | |
|
50 |
3Cr13 |
0.26-0.35 |
≤1.00 |
≤1.00 |
≤0.035 |
≤0.030 |
3) |
12.00-14.00 |
- |
- |
- |
- | |
|
51 |
Y3Cr13 |
0.26-0.40 |
≤1.00 |
≤1.25 |
≤0.035 |
≥0.15 |
3) |
12.00-14.00 |
1) |
- |
- |
- | |
|
52 |
3Cr13Mo |
0.28-0.35 |
≤0.80 |
≤1.00 |
≤0.035 |
≤0.030 |
3) |
12.00-14.00 |
0.50-1.00 |
- |
- |
- | |
|
53 |
4Cr13 |
0.36-0.45 |
≤0.60 |
≤0.80 |
≤0.035 |
≤0.030 |
3) |
12.00-14.00 |
- |
- |
- |
- | |
|
54 |
1Cr17Ni2 |
0.11-0.17 |
≤0.80 |
≤0.80 |
≤0.035 |
≤0.030 |
1.50-2.50 |
16.00-18.00 |
- |
- |
- |
- | |
|
55 |
7Cr17 |
0.60-0.75 |
≤1.00 |
≤1.00 |
≤0.035 |
≤0.030 |
3) |
16.00-18.00 |
4) |
- |
- |
- | |
|
56 |
8Cr17 |
0.75-0.95 |
≤1.00 |
≤1.00 |
≤0.035 |
≤0.030 |
3) |
16.00-18.00 |
4) |
- |
- |
- | |
|
57 |
9Cr18 |
0.90-1.00 |
≤0.80 |
≤0.80 |
≤0.035 |
≤0.030 |
3) |
17.00-19.00 |
4) |
- |
- |
- | |
|
58 |
11Cr17 |
0.95-1.20 |
≤1.00 |
≤1.00 |
≤0.035 |
≤0.030 |
3) |
16.00-18.00 |
4) |
- |
- |
- | |
|
59 |
Y11Cr17 |
0.95-1.20 |
≤1.00 |
≤1.25 |
≤0.035 |
≥0.15 |
3) |
16.00-18.00 |
4) |
- |
- |
- | |
|
60 |
9Cr18Mo |
0.95-1.10 |
≤0.80 |
≤0.80 |
≤0.035 |
≤0.030 |
3) |
16.00-18.00 |
0.40-0.70 |
- |
- |
- | |
|
61 |
9Cr18MoV |
0.85-0.95 |
≤0.80 |
≤0.80 |
≤0.035 |
≤0.030 |
3) |
17.00-19.00 |
1.00-1.30 |
- |
- |
V0.07-0.12 | |
|
沉淀硬化型 |
62 |
0Cr17Ni4Cu4Nb |
≤0.07 |
≤1.00 |
≤1.00 |
≤0.035 |
≤0.030 |
6.50-7.50 |
15.50-17.50 |
- |
3.00-5.00 |
- |
Nb 0.15-0.45 |
|
63 |
0Cr17Ni7Al |
≤0.09 |
≤1.00 |
≤1.00 |
≤0.035 |
≤0.030 |
6.50-7.50 |
16.00-18.00 |
- |
≤0.50 |
- |
Al 0.75-1.50 | |
|
64 |
0Cr15Ni7Mo2Al |
≤0.09 |
≤1.00 |
≤1.00 |
≤0.035 |
≤0.030 |
6.50-7.50 |
14.00-16.00 |
2.00-3.00 |
- |
- |
Al 0.75-1.50 | |
本文共分